DEKASEAL MS-2 SIGILL WHITE POLYMER ADHESIVE 290 ML

DEKASEAL MS-2 WHITE POLYMERIC ADHESIVE SEALANT 290 ML CARTRIDGE - UV resistant

DEKASYL MS-2 is the ideal compromise between adhesive and sealant for creating elastic connections between components that also require high adhesive strength (antennas and solar panels on the roof).

DEKASYL MS-2 glues and seals in a single treatment, does not weaken the material used and leaves no traces of connecting elements (screws or similar).

• Aluminum
• Polyester
• GFK (glass fibre reinforced plastic)
• PMMA (polymethyl methacrylate abb. PMMA or also acrylic glass) transparent thermoplastic
• Compensation for structural tolerances
• Glass
• Skylights - and windows
• Wheel fairings
• and much more

Repainting of the MS-2 adhesive sealant is possible after the film has formed.

The fields of application and use are multiple and can be expanded according to needs.

• Base material: MS Polymer
• Curing / Sealing: Moisture
• Specific weight: approximately 1.4 kg/litre
• Skin formation time (20°C/50% rel. LF): approx. 10 minutes
• Opening time (20°C/50% rel. LF): < 15 minutes
• Hardening after 24 hours (20°C/50% rel. LF): approx. 3 mm
• Shore A hardness (DIN 53505): approx. 55
• Volume change (DIN 52451): < 3%.
• Bond strength (Physical Rheometer MC100): approx. 300 Pa (Measure the maximum amount of adhesive that can be applied per m² without sagging)
• Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 Mpa
• Tensile stress at break (DIN 53504/ISO 37): approx. 2.6 MPa
• Elongation at break (DIN 53504/ISO 27): approx. 250%.
• Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa
• Tear resistance (DIN 53515/ISO 34): approx. 16 N/mm
• Solvent content: 0%.
• Isocyanate content: 0%.
• Temperature resistance: -40°C to +120°C
• Application temperature: from +5°C to +35°C
• Resistance to UV rays and atmospheric agents: excellent